Railroad track, or track for short, it is mainly used in the railroad. Railroad track cooperates with switch, so that the train can run safely. As we all known, railroad track is made up of two parallel rails, steel rails are fixed on the railway sleepers and ballast is under the railway sleepers. Railroad track is consisting of rail brace, steel rail, railway fish plate, railway fasteners, and etc. Railroad track is subjected to a variety of static load and dynamic load from vertical and lateral. Railroad track transfer all loads to the subgrade through the sleeper and track bed.
what are railroad track made of?
Railroad tracks are primarily made from high-quality, hot-rolled steel alloy (like medium-carbon steel) to withstand immense stress, featuring a specific I-beam shape for strength, with additives like manganese, vanadium, or chromium for enhanced durability and hardness, often followed by heat treatment for extra toughness and wear resistance.
The chemical composition of train track steel
| No. | Element | Function |
|---|---|---|
| 1 | C | Improve the strength, hardness, and wear resistance of the rail. The carbon content of domestic rails is 0.65% to 0.82%. When the carbon content is relatively high, the steel becomes brittle, and its plasticity index will be significantly reduced. At the same time, it will increase the chance of white spots in the steel. |
| 2 | Si | It is easy to combine with oxidation and can play the role of removing bubbles in the metal. The steel contains an appropriate amount of silicon, which can improve the hardness and wear resistance of the steel. The content of domestic rail steel is generally 0159-0.9%, but too much content will make the steel hard and brittle, and it is easy to produce pores in the weld. |
| 3 | Mn | It is a beneficial element that can improve the strength and wear resistance of steel and increase the toughness of steel. It can remove harmful iron oxide and sulfide inclusions in the steel. The manganese content is generally controlled between 0.6% and 1.54%. Steel with a manganese content of more than 1.2% is called medium manganese steel, and its wear resistance is very high. |
| 4 | Cu | It is a beneficial element. Steel contains a small number of copper compounds, which can improve the fatigue resistance and corrosion resistance of steel. The copper content of domestic steel rails is generally between 0.10% and 0.40%. If the rolling process of the copper-containing rail is not good, fish-like cracks will occur on the surface of the rail |
| 5 | P | It is a harmful element. The biggest hazard of phosphide is to reduce the plasticity and toughness of the steel. Especially at low temperatures, the cold brittleness of the steel increases, which easily leads to broken rails, and its content is controlled at no more than 0.04% |
| 6 | S | The sulfur is a harmful element. It is often left in the steel in the form of granules. When the rail is rolled, it is rolled together with the steel into sheets, which causes delamination or longitudinal cracks in the rail. The amount of sulfur is controlled at no more than 0.05% |
Common materials for steel rail：
| Steel Grade | C(%) | Si | Mn | Cr | V | P | S | Tensile Strength (Rm/MPa) |
| U71Mn | 0.65~0.76 | 0.15~0.58 | 0.70~1.40 | – | – | ≤0.035 | ≤0.030 | ≥880 |
| U75V | 0.71~0.80 | 0.50~0.80 | 0.75~1.05 | – | 0.04~0.12 | ≤0.035 | ≤0.030 | ≥980 |
| U78CrV | 0.72~0.82 | 0.50~0.80 | 0.70~1.05 | 0.30~0.50 | 0.04~0.12 | ≤0.035 | ≤0.030 | ≥1080 |
| U77MnCr | 0.72~0.82 | 0.10~0.50 | 0.80~1.10 | 0.25~0.40 | – | ≤0.035 | ≤0.025 | ≥980 |
| U76CrRE | 0.71~0.81 | 0.50~0.80 | 0.80~1.10 | 0.25~0.35 | 0.04~0.08 | ≤0.035 | ≤0.025 | ≥1080 |
As a professional rail fastener supplier, GNEE RAIL can provide different standard steel rail such as GB,American, BS, UIC, DIN, JIS, Australian and South Africa which used in railway lines, cranes and coal mining.
| Standard | Sepc. | Material Typical Grade |
| UIC860 | UIC54 | 700,900A,900B |
| UIC60 | ||
| EN13674.1 | 5.00E+02 | R200,R350HT,R260Mn,R35LHT,R320Cr,R370CrHT |
| 5.40E+02 | ||
| 6.00E+02 | ||
| 6.00E+03 | ||
| BS-11-1985 | BS80A | 700,900A,900B |
| BS90A | ||
| BS100A | ||
| AREMA | 115RE | SS,HH,LA,IH |
| 136RE | ||
| ASCE60 | U71Mn | |
| ASCE85 | U71Mn | |
| GB 2585-2007 | 50kg/m | U71Mn |
| 60kg/m | U75V | |
| 75kg/m | ||
| TB/T2344-2012 | 50kg/m | U71Mn,U75V,U77MnCr |
| 60kg/m | U78CrV | |
| 75kg/m | ||
| GB 11264-1989 | 8kg/m | Q235 |
| 12kg/m | Q235 | |
| 15kg/m | 55Q, Q235 | |
| 18kg/m | 55Q, Q235 | |
| 22kg/m | 55Q, Q235 | |
| 24kg/m | 55Q, Q235 | |
| 30kg/m | 55Q, Q235 | |
| 38kg/m | 50Mn, U71Mn | |
| 43kg/m | 50Mn, U71Mn | |
| GB Crane rails | QU70 | U71Mn |
| QU80 | U71Mn | |
| QU100 | U71Mn | |
| QU120 | U71Mn |